磷酸鈦氧鉀(KTP)
磷酸鈦氧鉀(KTP)最常用于倍頻Nd:YAG及其他摻Nd晶體的激光，特別是在中低功率密度的激光器中。到目前為止，利用KTP進(jìn)行腔內(nèi)與腔外倍頻的摻Nd晶體的激光器，在逐步取代可見(jiàn)光染料激光和可調(diào)藍(lán)寶石激光器。廣泛使用實(shí)驗(yàn)室和醫(yī)學(xué)系統(tǒng), 射程探測(cè)器，激光雷達(dá)，光通信和工業(yè)激光系統(tǒng)。
Advantages:- Large Nonlinear Optical (NLO) Coefficients
- Wide Angular Bandwidth and Small Walk-off Angle
- Broad Temperature and Spectral Bandwidth
- High Electro-Optic (E-O) Coefficient and Low Dielectric Constant
- Large Figure of Merit for an Optical Waveguide Modulator
- Nonhygroscopic, Good Chemical and Mechanical Properties
Capabilities:
|
Aperture:
|
2x2 ~ 10x10mm
|
|
Lenght:
|
0.1 - 20mm
|
|
Cutting Angle q and f:
|
Determined by different kinds of homonic generartion
|
|
Phase matching type:
|
Type I or Type II
|
|
End Configuration:
|
Plano/Plano or Brewst/Brewst or Specified
|
Specifications:
|
Angle tolerance:
|
Δθ< ± 0.5°; Δφ< ±0.5°
|
|
Dimensional Tolerance:
|
(W ± 0.1mm) x (H ± 0.1mm) x (L + 0.2mm/-0.1mm)
|
|
Flatness:
|
<λ/8 at 633nm
|
|
Surface Quality:
|
10/5 Scracth/Dig
|
|
Parallelism:
|
< 20 arc seconds
|
|
Perpendicularity:
|
< 5 arc minutes
|
|
Wavefront Distortion:
|
<λ/8 at 632.8nm
|
|
Clear Aperture:
|
Central 95%
|
|
Chamfer:
|
0.15x45°
|
|
Coating:
|
a) * S1,S2: AR @ 1064 nm R<0.1% & 532nm R<0.25%
b) * S1:HR @ 1064nm R>99.8% & HT@ 808nm T>95% S2:AR @ 1064 nm R<0.1% & 532nm R<0.25% |
Prorerties:
|
Crystal structure
|
Orthorhombic, point group mm2
|
|||
|
Melting point
|
1172°C incongruent
|
|||
|
Cell parameters
|
a=6.404?, b=10.616?, c=12.814?, Z=8
|
|||
|
Curie point
|
936°C
|
|||
|
Mohs hardness
|
~5
|
|||
|
Density
|
3.01 g/cm3
|
|||
|
Color
|
colorless
|
|||
|
Hygroscopic susceptibility
|
no
|
|||
|
Specific heat
|
0.1643 caλ/g.°C
|
|||
|
Thermal conductivity
|
0.13 W/cm/°K
|
|||
|
Electrical conductivity
|
3.5x10-8 s/cm (c-axis, 22°C, 1KHz)
|
|||
|
Transmitting range
|
350nm~4500nm
|
|||
|
Refractive indices
|
-
|
nx
|
ny
|
nz
|
|
1064nm
|
1.7377
|
1.7453
|
1.8297
|
|
|
532nm
|
1.7780
|
1.7886
|
1.8887
|
|
|
Absorption coefficients
|
a < 1%/cm @1.064μ m and 0.532μ m
|
|||
|
Phase matchable range
|
0.984 - 3.4 μ m
|
|||
|
Therm-optic coefficients
|
dnx/dT=1.1x10-5/°C, dny/dT=1.3x10-5/oC, dnz/dT=1.6x10-5/°C
|
|||
|
Nonlinear optical coefficients
|
d31=2.54pm/V, d31=4.35pm/V, d31=16.9pm/V
d24=3.64pm/V, d15=1.91pm/V at 1.064 mm deff(II)≈(d24 - d15)sin2Φsin2Θ - (d15sin2Φ?+ d24cos2Φ)sinΘ |
|||
|
Electro-optic coefficients
|
-
|
Low frequency(pm/V)
|
High requency(pm/V)
|
|
|
γ13
γ23
γ33 γ51 γ42 |
9.5
15.7 36.3 7.3 9.3 |
8.8
13.8 35.0 6.9 8.8 |
||
|
Dielectric constant
|
eeff=13
|
|||
Sellmeier equations
nx2=3.0065+0.03901/(l2-0.04251)-0.01327l2
ny2=3.0333+0.04154/(l2-0.04547)-0.01408l2
nz2=3.3134+0.05694/(l2-0.05658)-0.01682l2
Note: Kinds of sizes, coating are available upon request.